Your present position:Home >> Products >> Tempered Solar Glass

2.0mm Half-Tempered Glass for

    • 2.0mm Half-Tempered Glass for
Product Details:

Low Iron ARC Temper Solar Glass with CE,UL,ISOcombined with nanometer anti-reflective coating technology,increase solar transmittance by way of decreasing light reflectance and improve the solar  cell phtotelectric conversion efficiency.Meanwhile,it reduces the reflected glare of the glass and the pollution caused by the reflectance to the environment. The hydrophobic behavior of the AR coating could in some degree protect the dust and dirt from shading the light and improve the cleaning performance of the glass. With the outstanding characteristics of the high solar lights transmittance, the low reflectance, the low iron, the high mechanical strenght and the high flatnessit is one of the indispensable important parts of solar cell and has been widely used to photovoltaic power generation all over the world.


ProductsLow Iron ARC Temper Solar Glass with CE,UL,ISO
Thickness3.2mm,4.0mm
SizeCan be customized,maximum size:1200*2200mm
Solar transmittance3.2mm≥93.8%,with AR coating
ApplicationsFor solar cell module
Payment termsT/T
DeliveryWithin 15 days after receiving the deposit 
MOQ2500 sqm
PortShanghai


Features of our Low Iron ARC Temper Solar Glass with CE,UL,ISO:
1.     High solar lights transmittance
2.     The low reflectance: visible light reflectance is less than 7.30%
3.     Low iron:glass has only 0.012% of iron content;
4.     High intensity,the strength is 3-5 times of ordinary annealed glass
5.     Wind pressure resistance: the wind pressure resistance is 1.5-3 times of ordinary annealed glass;
6.     Heat shock resistance: the heat shock resistance is 3 times of ordinary annealed glass;
7.     Safety:if it is broken, it usually breaks into relatively small pieces, which are less likely to cause serious injury.


Test Standards Test method Results 
1 Appearance EN1096-2 Surface is clean, no scratches,spots or pinhole Qualified 
2 Light transmittance ISO 9050 The ratio after coating is higher than before >2.5>2.6 
3 Adhesion ASTMD3359 The cutting edge is very smooth , no grid slide, 0 level
4 Pencil hardness ASTMD3363 No thickness of film which scratched by pencil more than 3mm≥6H 
5 Salt spray test EN1096-2With 5%(±1)NaC1,under 35ºC,last 4-9days,record  the data before and after the test, T<1.0 4 days,      T=0.57   9 days,      T=0.91 
6 Thermal CycleIEC61215/10 Keep the temperature between -40ºC and 85ºC,±2ºC,200 times,(around 1000 hours),record  the data before and after the test,T<1.0 T=0.48 
7 Muggle Test IEC61215/10 Under 85ºC,±2ºC,relative humidity is 85ºC,±5ºC,around 1000 hours,record  the data before and after the test,T<1.0 T=0.63
8 Wet-cold test IEC61215/10 Humidity is 855ºC,temperature is 85ºC,±2ºC,fall to -40ºC,cycle for 10 times.Record  the data before and after the test,T<1.0 T=0.80 
9 Outdoor exposure IEC61215/10 Test with the moniter in outdoor temperature,total radiation need to be 60kmh·m-2 .Record  the data before and after the test,T<1.0 T=0.59 
10 Mechanical Loading IEC61215/10 Adding the load to 2400Pa and make it distributed.Keep 2-3 times;the layer wasn't broken and no serious defects in appearance Qualified 